Pore solution in alkali-activated slag cement pastes. Relation to the composition and structure of calcium silicate hydrate
In this work, the relationship between the composition of pore solution in alkali-activated slag cement (AAS) pastes activated with different alkaline activator, and the composition and structure of the main reaction products, has been studied. Pore solution was extracted from hardened AAS pastes. The analysis of the liquids was performed through different techniques: Na, Mg and Al by atomic absorption (AA), Ca ions by ionic chromatography (IC) and Si by colorimetry; pH was also determined. The solid phases were analysed by XRD, FTIR, solid-state {sup 29}Si and {sup 27}Al NMR and BSE/EDX. The most significant changes in the ionic composition of the pore solution of the AAS pastes activated with waterglass take place between 3 and 24 h of reaction. These changes are due to the decrease of the Na content and mainly to the Si content. Results of {sup 29}Si MAS NMR and FTIR confirm that the activation process takes place with more intensity after 3 h (although at this age, Q{sup 2} units already exist). The pore solution of the AAS pastes activated with NaOH shows a different evolution to this of pastes activated with waterglass. The decrease of Na and Si contents progresses with time. The nature of the alkaline activator influences the structure and composition of the calcium silicate hydrate formed as a consequence of the alkaline activation of the slag. The characteristic of calcium silicate hydrate in AAS pastes activated with waterglass is characterised by a low structural order with a low Ca/Si ratio. Besides, in this paste, Q{sup 3} units are detected. The calcium silicate hydrate formed in the pastes activated with NaOH has a higher structural order (higher crystallinity) and contains more Al in its structure and a higher Ca/Si ratio than those obtained with waterglass.
- OSTI ID:
- 20658332
- Journal Information:
- Cement and Concrete Research, Vol. 34, Issue 1; Other Information: DOI: 10.1016/S0008-8846(03)00254-0; PII: S0008884603002540; Copyright (c) 2003 Elsevier Science B.V., Amsterdam, The Netherlands, All rights reserved; Country of input: International Atomic Energy Agency (IAEA); ISSN 0008-8846
- Country of Publication:
- United States
- Language:
- English
Similar Records
Investigation on a green olivine nano-silica source based activator in alkali activated slag-fly ash blends: Reaction kinetics, gel structure and carbon footprint
Assessment of calcium addition on the removal of U(VI) in the alkaline conditions created by NH3 gas