Properties of ternary Sn-Ag-Bi solder alloys. Part 2: Wettability and mechanical properties analyses
Bismuth additions of 1% to 10% were made to the 96.5Sn-3.5Ag (wt.%) alloy in a study to develop a Sn-Ag-Bi ternary composition. Thermal properties and microstructural analyses of selected alloy compositions were reported in Part 1. Wettability and mechanical properties are described in this paper. Contact angle measurements demonstrated that Bi additions improved wetting/spreading performance on Cu; a minimum contact angle of 31 {+-} 4{degree} was observed with 4.83 wt.% Bi addition. Increasing the Bi content of the ternary alloy raised the Cu/solder/Cu solder joint shear strength to 81 MPa as determined by the ring-and-plug tests. TEM analysis of the 91.84Sn-3.33Ag-4.83Bi composition presented in Part 1 indicated that the strength improvement was attributed to solid-solution and precipitation strengthening effects by the Bi addition residing in the Sn-rich phase. Microhardness measurements of the Sn-Ag-Bi alloy, as a function of Bi content, reached maximum values of 30 (Knoop, 50 g) and 110 (Knoop, 5g) for Bi contents greater than approximately 4--5 wt.%.
- Research Organization:
- Sandia National Labs., Albuquerque, NM (US)
- Sponsoring Organization:
- USDOE
- DOE Contract Number:
- AC04-94AL85000
- OSTI ID:
- 20000474
- Journal Information:
- Journal of Electronic Materials, Vol. 28, Issue 10; Other Information: PBD: Oct 1999; ISSN 0361-5235
- Country of Publication:
- United States
- Language:
- English
Similar Records
Development of Sn-based, low melting temperature Pb-free solder alloys.
Prototype circuit boards assembled with non-lead bearing solders