Low aluminum content permeation barrier coatings for DIN 1.4914 martensitic steel (MANET)
Journal Article
·
· Fusion Technology
OSTI ID:196776
- European Commission, Ispra (Italy)
This paper describes the production and permeation measurements of three different aluminide coatings on the surface of MANET II stainless steel. The coatings were produced by vacuum plasma spraying pure aluminium ({approx}= 100{mu}m) on to the steel, which was subsequently heat treated to produce an aluminide layer on the MANET. The relationship between the aluminum content of the coatings and their effectiveness as permeation barriers, due to the greater or lower resistance to crack formation was manifest. The coatings with a lower aluminum content presented the largest permeation reduction (2 orders of magnitude). 10 refs., 6 figs., 4 tabs.
- OSTI ID:
- 196776
- Report Number(s):
- CONF-950506-; ISSN 0748-1896; TRN: 96:001398-119
- Journal Information:
- Fusion Technology, Vol. 28, Issue 3 pt 2; Conference: 5. topical meeting on tritium technology in fission, fusion and isotopic applications, Ispra (Italy), 28 May - 3 Jun 1995; Other Information: PBD: Oct 1995
- Country of Publication:
- United States
- Language:
- English
Similar Records
Hydrogen permeation behavior of hot-dip aluminized manet steel
Evaluation of Oxidation and Hydrogen Permeation of Al Containing Duplex Stainless Steels
Characterization of aluminide coatings formed on 1.4914 and 316L steels by hot-dipping in molten aluminium
Journal Article
·
Sun Oct 01 00:00:00 EDT 1995
· Fusion Technology
·
OSTI ID:196776
Evaluation of Oxidation and Hydrogen Permeation of Al Containing Duplex Stainless Steels
Journal Article
·
Fri Jun 17 00:00:00 EDT 2005
· Materials Science and Engineering
·
OSTI ID:196776
Characterization of aluminide coatings formed on 1.4914 and 316L steels by hot-dipping in molten aluminium
Journal Article
·
Sat Feb 15 00:00:00 EST 1997
· Scripta Materialia
·
OSTI ID:196776