Behavior of painted steel and aluminum sheet in laboratory automotive corrosion tests
- Bethlehem Steel Corp., PA (United States). Homer Research Labs.
Because of environmental concern and government pressure, automakers are exploring ways to increase the fuel economy of vehicles. Mass reduction can be achieved by substituting plastics, aluminum, or high-strength steel for ordinary grades of steel in the autobody. Estimates of fuel economy increases range from 3% to 7% for each 10% reduction in mass. The use of aluminum for mass reduction currently is receiving considerable attention. Cold-rolled steel, electrogalvanized steel (60 g/m{sup 2} coating), and three aluminum alloy sheet products (Al 2036, Al 5182, and Al 6111) were painted with a full automotive paint system. These materials were tested in two laboratory cyclic corrosion test environments, GM9540P(B) and CCT-IV. Resistance to cosmetic corrosion was measured in terms of underfilm paint delamination on scribed, flat panels. Crevice corrosion resistance was determined in terms of pitting on lapped panels of like materials, and galvanic corrosion resistance was determined in terms of pitting on lapped panels of unlike materials. Cosmetic corrosion of the aluminum alloys was found to be much better than that of cold-rolled steel and slightly better than that of electrogalvanized steel. The CCT-IV test was found to be more severe than GM9540P(B) for cosmetic corrosion, but GM9540P(B) was more severe for galvanic corrosion. Galvanic current measurements indicated the difference was related to the salt solutions used in each test. The aluminum alloys were prone to crevice corrosion and to galvanic corrosion when coupled to steel. Results indicated that comparative evaluations of the corrosion resistance of these materials must take into account the possibility of crevice and galvanic effects.
- Sponsoring Organization:
- USDOE
- OSTI ID:
- 187043
- Journal Information:
- Corrosion, Vol. 52, Issue 1; Other Information: PBD: Jan 1996
- Country of Publication:
- United States
- Language:
- English
Similar Records
Effects of salt deposition and temperature on polarization resistance of steel and the galvanic current of steel-aluminum couples during exposure to cyclic humidity
In-situ electrochemical study of corrosion of steel and aluminum/steel couples during cyclic corrosion test