Interstrand Coupling Properties of LARP High Gradient Quadrupole Cables in Response to Variations in Cable Design and Heat Treatment Condition
- The Ohio State Univ., Columbus, OH (United States)
- Lawrence Berkeley National Lab. (LBNL), Berkeley, CA (United States)
- Univ. of Twente, Enschede (The Netherlands)
Calorimetric measurement of coupling loss versus frequency has been measured on two sets of cored and uncored large Hadron Collider Accelerator Research Program high gradient quadrupole Nb3Sn Rutherford cables. Studied are the responses of the resulting interstrand contact resistances (ICR) to variation of stainless-steel (SS) core width and position and to variation of reaction-heat-treatment (RHT) condition. One pair of cables (an early HQ-series type) with and without core had received RHT under 20-MPa uniaxial face-on pressure. Another set of cables (recent QXF type) furnished with SS cores of various widths had received RHT under ambient pressure. The results were displayed as cable-cross-sectional micrographs and plots of ICR versus percent core coverage (W). The HQ cables were tightly compacted and produced results consistent with a previously expected continuous ICR versus W variation. Furthermore, the QXF cables were uncompacted such that their upper and lower layers were separated by what is referred to as a full-width 'pseudocore;' as a result, their ICRs were independent of the widths of the SS cores. Compaction versus noncompaction is discussed and future research directions are suggested.
- Research Organization:
- Lawrence Berkeley National Laboratory (LBNL), Berkeley, CA (United States)
- Sponsoring Organization:
- USDOE Office of Science (SC), High Energy Physics (HEP)
- Grant/Contract Number:
- AC02-05CH11231
- OSTI ID:
- 1510744
- Journal Information:
- IEEE Transactions on Applied Superconductivity, Vol. 27, Issue 4; ISSN 1051-8223
- Publisher:
- Institute of Electrical and Electronics Engineers (IEEE)Copyright Statement
- Country of Publication:
- United States
- Language:
- English
Similar Records
Influence of Compaction During Reaction Heat Treatment on the Interstrand Contact Resistances of Nb3Sn Rutherford Cables for Accelerator Magnets
Calorimetric measurements of the effect of nickel and stabrite coatings and resistive cores on AC loss in accelerator cables under fixed pressure