Ni and Cr addition to alloy waste forms to reduce radionuclide environmental releases
- Savannah River Site (SRS), Aiken, SC (United States). Savannah River National Lab. (SRNL)
Reference alloy waste forms (RAW) were fabricated and underwent hybrid corrosion/immersion testing to parameterize the ANL analytical oxidative-dissolution model to enable the calculation of fractional release rates and to determine the effectiveness of Ni and Cr trim additions in reducing release rates of radionuclide surrogates. Figure 1 shows the prototypical multiphase microstructure of the alloys with each phase type contributing about equally to the exposed surface area. The waste forms tested at SRNL were variations of the RAW-6 formulation that uses HT9 as the main alloy component, and are meant to enable evaluation of the impact of Ni and Cr trim additions on the release rates of actinides and Tc-99. The test solutions were deaerated alkaline and acidic brines, ranging in pH 3 to pH 10, representing potential repositories with those conditions. The testing approach consisted of 4 major steps; 1) bare surface corrosion measurements at pH values of 3, 5, 8, and 10, 2) hybrid potentiostatic hold/exposure measurements at pH 3, 3) measurement of radionuclide concentrations and relations to anodic current from potentiostatic holds, and 4) identification of corroding phases using SEM/EDS of electrodes.
- Research Organization:
- Savannah River Site (SRS), Aiken, SC (United States)
- Sponsoring Organization:
- USDOE
- DOE Contract Number:
- DE-AC09-08SR22470
- OSTI ID:
- 1353011
- Report Number(s):
- SRNL-STI-2016-00602
- Country of Publication:
- United States
- Language:
- English
Similar Records
Corrosion Testing of Carbon Steel Exposed to Sludge Heel Chemical Cleaning Solutions - 16109
Effects of variations of carbon, sulfur, and phosphorus on the corrosion behavior of alloy 600