Improved performance by morphology control via fullerenes in PBDT-TBT-alkoBT based organic solar cells
- South Dakota State Univ., Brookings, SD (United States)
- Oak Ridge National Lab. (ORNL), Oak Ridge, TN (United States)
In this work, we report improved performance by controlling morphology using different fullerene derivatives in poly{2-octyldodecyloxy-benzo[1,2-b;3,4-b]dithiophene-alt-5,6-bis(dodecyloxy)-4,7- di(thieno[3,2-b]thiophen-2-yl)-benzo[c][1,2,5]thiadiazole} (PBDT-TBT-alkoBT) based organic solar cells. PC60BM and PC70BM fullerenes were used to investigate the characteristic change in morphology and device performance. Fullerene affects device efficiency by changing active layer morphology. PC70BM with broader absorption than PC60BM resulted in reduced device performance which was elucidated by the intermixed granular morphology separating each larger grain in the PC70BM/polymer composite layer which created higher density of traps. However after adding additive 1,8-diiodooctane (DIO), the fibrous morphology was observed due to reduced solubility of polymer and increased solubility of PC70BM in chloroform. The fibrous morphology improved charge transport leading to increase in overall device performance. Atomic force microscopies (AFM), photo induced charge extraction by linearly increasing voltage (photo-CELIV), and Kelvin prove force microscope (KPFM) were used to investigate nanoscale morphology of active layer with different fullerene derivatives. For PC60BM based active layer, AFM images revealed dense fibrous morphology and more distinct fibrous morphology was observed by adding DIO. The PC70BM based active layer only exhibited intermixed granular morphology instead of fibrous morphology observed in PC60BM based active layer. However, addition of DIO in PC70BM based active layer led to fibrous morphology. When additive DIO was not used, a wider distribution of surface potential was observed for PC70BM than PC60BM based active layer by KPFM measurements, indicating 2 polymer and fullerene domains are separated. When DIO was used, narrower distribution of surface potential for both PC70BM and PC60BM based active layers was observed. Photo-CELIV experiment showed larger extracted charge carrier density and mobility in PC70BM/DIO film.
- Research Organization:
- Oak Ridge National Laboratory (ORNL), Oak Ridge, TN (United States). Center for Nanophase Materials Sciences (CNMS)
- Sponsoring Organization:
- USDOE Office of Science (SC)
- Grant/Contract Number:
- AC05-00OR22725
- OSTI ID:
- 1286906
- Journal Information:
- Journal of Materials Chemistry. A, Vol. 3, Issue 29; ISSN 2050-7488
- Publisher:
- Royal Society of ChemistryCopyright Statement
- Country of Publication:
- United States
- Language:
- English
Web of Science
Progress and development in structural and optoelectronic tunability of supramolecular nonbonded fullerene assemblies
|
journal | January 2019 |
Similar Records
The Impact of Fullerene Structure on its Miscibility with P3HT and its Correlation of Performance in Organic Photovoltaics.
The Impact of Fullerene Structure on Its Miscibility with P3HT and Its Correlation of Performance in Organic Photovoltaics