The morphology of blends of linear and branched polyethylenes in solid state by small-angle scattering
- Oak Ridge National Lab., TN (United States)
- Florida State Univ., Tallahassee, FL (United States); and others
We have used small-angle neutron and x-ray scattering (SANS And SAXS) to investigate the solid state morphology of blends of high-density and low-density polyethylenes (HDPE and LDPE). The blends are homogenous in the melt as demonstrated by SANS using the contrast obtained by deuterating the linear polymer, though they phase segregate on slow cooling (0.75{degree}C/min). For high concentrations ({theta} {ge} 0.5) of linear polymer, there are separate stacks of HDPE and LDPE lamellae, as indicated by 2-peak SAXS curves. For predominantly branched blends, the phase separation is less complete, and the components are separated within the same lamellar stack, with alternating HDPE and LDPE lamellae. Moreover, the phases no longer consist of the pure components and the HDPE lamellae contain up to 15% LDPE. Rapid quenching into dry-ice/acetone (-78{degree}C) produces only one lamellar stack over the whole concentration range. The blends show extensive cocrystallization with a tendency for the branched material to be preferentially located in the amorphous regions. For high concentrations ({theta} {ge} 0.5) of HDPE-D the overall scattering length density is high and the excess concentration of LDPE between the lamellae enhances the contrast between the crystalline and amorphous phases. Thus, the interlamellar spacing (long period) is clearly visible in the SANS pattern. The blend morphology is a strong function of the quench rate and samples quenched less rapidly (e.g., into water at 23{degree}C) show a similar morphology to slowly cooled samples.
- OSTI ID:
- 126889
- Report Number(s):
- CONF-950402-; TRN: 95:006086-0942
- Resource Relation:
- Conference: 209. American Chemical Society (ACS) national meeting, Anaheim, CA (United States), 2-6 Apr 1995; Other Information: PBD: 1995; Related Information: Is Part Of 209th ACS national meeting; PB: 2088 p.
- Country of Publication:
- United States
- Language:
- English
Similar Records
The morphology of blends of linear and branched polyethylenes
The morphology of blends of linear and branched polyethylenes by small-angle neutron and x-ray scattering