Effect of Spacer Length of Siloxane-Terminated Side Chains on Charge Transport in Isoindigo-Based Polymer Semiconductor Thin Films
Journal Article
·
· Advanced Functional Materials
- Department of Chemical Engineering, Stanford University, Stanford CA 94305-5025 USA; Department of Chemistry, Purdue University, West Lafayette IN 47907 USA
- Department of Chemical Engineering, Stanford University, Stanford CA 94305-5025 USA; Department of Chemical Engineering, National Taiwan University, Taipei 10617 Taiwan
- Department of Chemical Engineering, Stanford University, Stanford CA 94305-5025 USA; Department of Chemical & Biomolecular Engineering, University of Illinois at Urbana−Champaign, 600 South Mathews Avenue Urbana IL 61801 USA
- Department of Chemical Engineering, Stanford University, Stanford CA 94305-5025 USA
- Department of Chemical Engineering, Stanford University, Stanford CA 94305-5025 USA; Department of Chemistry, Tsinghua University, Beijing 100084 China
- Department of Chemical Engineering, National Taiwan University, Taipei 10617 Taiwan
- Research Organization:
- SLAC National Accelerator Lab., Menlo Park, CA (United States)
- Sponsoring Organization:
- USDOE
- DOE Contract Number:
- AC02-76SF0051
- OSTI ID:
- 1261195
- Journal Information:
- Advanced Functional Materials, Vol. 25, Issue 23; ISSN 1616-301X
- Country of Publication:
- United States
- Language:
- English
Similar Records
Symmetry Breaking in Side Chains Leading to Mixed Orientations and Improved Charge Transport in Isoindigo-alt-Bithiophene Based Polymer Thin Films
Siloxane-Terminated Solubilizing Side Chains: Bringing Conjugated Polymer Backbones Closer and Boosting Hole Mobilities in Thin-Film Transistors
Unraveling the Main Chain and Side Chain Effects on Thin Film Morphology and Charge Transport in Quinoidal Conjugated Polymers
Journal Article
·
Fri Jul 21 00:00:00 EDT 2017
· ACS Applied Materials and Interfaces
·
OSTI ID:1261195
+7 more
Siloxane-Terminated Solubilizing Side Chains: Bringing Conjugated Polymer Backbones Closer and Boosting Hole Mobilities in Thin-Film Transistors
Journal Article
·
Fri Aug 30 00:00:00 EDT 2013
· J. Am. Chem. Soc. 133:20130,2011
·
OSTI ID:1261195
+2 more
Unraveling the Main Chain and Side Chain Effects on Thin Film Morphology and Charge Transport in Quinoidal Conjugated Polymers
Journal Article
·
Tue Jun 05 00:00:00 EDT 2018
· Advanced Functional Materials
·
OSTI ID:1261195
+8 more