Mechanochemical synthesis of Nd2Fe14B alloy with high coercivity
Journal Article
·
· Journal of Alloys and Compounds
High coercivity nanocrystalline Nd2Fe14B particles were synthesized by mechanochemical processing involving the reduction of Nd2O3 with Ca in presence of Fe-B and Fe. The as-milled powder shows amorphous structure and subsequent heat treatment results in formation of nanocrystalline Nd2Fe14B. The resulting powder does not only consist of Nd2Fe14B but also some Nd-rich phase. The optimally heat treated sample exhibits coercivity of more than 12 kOe. (C) 2012 Elsevier B.V. All rights reserved.
- Sponsoring Organization:
- USDOE Advanced Research Projects Agency - Energy (ARPA-E)
- OSTI ID:
- 1211053
- Journal Information:
- Journal of Alloys and Compounds, Vol. 543; ISSN 0925-8388
- Country of Publication:
- United States
- Language:
- English
Similar Records
Magnetic property and microstructure of single crystalline Nd2Fe14B ultrafine particles ball milled from HDDR powders
Textured Nd2Fe14B flakes with enhanced coercivity
Single-crystal and textured polycrystalline Nd2Fe14B flakes with a submicron or nanosize thickness
Journal Article
·
Thu Aug 01 00:00:00 EDT 2013
· Journal of Magnetism and Magnetic Materials
·
OSTI ID:1211053
+3 more
Textured Nd2Fe14B flakes with enhanced coercivity
Journal Article
·
Sun Apr 01 00:00:00 EDT 2012
· Journal of Applied Physics
·
OSTI ID:1211053
+2 more
Single-crystal and textured polycrystalline Nd2Fe14B flakes with a submicron or nanosize thickness
Journal Article
·
Wed Feb 01 00:00:00 EST 2012
· Acta Materialia
·
OSTI ID:1211053
+2 more