The Impacts of Cation Stoichiometry and Substrate Surface Quality on Nucleation, Structure, Defect Formation, and Intermixing in Complex Oxide Heteroepitaxy–LaCrO3 on SrTiO3(001)
Our ability to design and fabricate electronic devices with reproducible properties using complex oxides is critically dependent on our ability to controllably synthesize these materials in thin-film form. Structure-property relationships are intimately tied to film and interface composition. Here we report on the effects of cation stoichiometry in LaCrO3 heteroepitaxial films prepared using molecular beam epitaxy. We show that LaCrO3 films grow pseudomorphically on SrTiO3(001) over an wide range of La-to-Cr atom ratios. However, the growth mode and structural quality are sensitive to the La-to-Cr ratio, with La-rich films being of considerably lower structural quality than Cr-rich films. Cation mixing occurs at the interface for all La-to-Cr ratios investigated, and is not quenched by deposition at ambient temperature. Indiffused La atoms occupy Sr sites in the substrate. The presence of defects in the SrTiO3 substrate is implicated in promoting La indiffusion by comparing the properties of LaCrO3/SrTiO3 with those of LaCrO3/Si, both prepared at ambient temperature. Additionally, pulsed laser deposition is shown to result in more extensive interfacial mixing than molecular beam epitaxy for deposition at ambient temperature on Si.
- Research Organization:
- Pacific Northwest National Lab. (PNNL), Richland, WA (United States). Environmental Molecular Sciences Lab. (EMSL)
- Sponsoring Organization:
- USDOE
- DOE Contract Number:
- AC05-76RL01830
- OSTI ID:
- 1133243
- Report Number(s):
- PNNL-SA-89831; 47425; 11592; 44701; 35200; KC0203020; KP1704020; KC0304030
- Journal Information:
- Advanced Functional Materials, 23(23):2953–2963, Journal Name: Advanced Functional Materials, 23(23):2953–2963
- Country of Publication:
- United States
- Language:
- English
Similar Records
Epitaxial growth, structure and intermixing at the LaAlO3/SrTiO3 interface as the film stoichiometry is varied
LaCrO3 heteroepitaxy on SrTiO3(001) by molecular beam epitaxy