Temperature-Dependent Photoluminescence Imaging and Characterization of a Multi-Crystalline Silicon Solar Cell Defect Area
Photoluminescence (PL) imaging is used to detect areas in multi-crystalline silicon that appear dark in band-to-band imaging due to high recombination. Steady-state PL intensity can be correlated to effective minority-carrier lifetime, and its temperature dependence can provide additional lifetime-limiting defect information. An area of high defect density has been laser cut from a multi-crystalline silicon solar cell. Both band-to-band and defect-band PL imaging have been collected as a function of temperature from {approx}85 to 350 K. Band-to-band luminescence is collected by an InGaAs camera using a 1200-nm short-pass filter, while defect band luminescence is collected using a 1350-nm long pass filter. The defect band luminescence is characterized by cathodoluminescence. Small pieces from adjacent areas within the same wafer are measured by deep-level transient spectroscopy (DLTS). DLTS detects a minority-carrier electron trap level with an activation energy of 0.45 eV on the sample that contained defects as seen by imaging.
- Research Organization:
- National Renewable Energy Lab. (NREL), Golden, CO (United States)
- Sponsoring Organization:
- USDOE Office of Energy Efficiency and Renewable Energy Solar Energy Technologies Program
- DOE Contract Number:
- AC36-08GO28308
- OSTI ID:
- 1049626
- Resource Relation:
- Conference: [Proceedings] 37th IEEE Photovoltaic Specialists Conference (PVSC '11), 19-24 June 2011, Seattle, Washington; Related Information: See NREL/CP-5200-50706 for preprint
- Country of Publication:
- United States
- Language:
- English
Similar Records
Defect-Band Emission Photoluminescence Imaging on Multi-Crystalline Si Solar Cells
Defect-Band Emission Photoluminescence Imaging on Multi-Crystalline Si Solar Cells: Preprint