Combinatorial Block Copolymer Ordering on Tunable Rough
Morphology control of block copolymer (BCP) thin films through substrate interaction via controlled roughness parameters is of significant interest for numerous high-tech applications ranging from solar cells to high-density storage media. While effects of substrate surface energy (SE) and roughness (R) on BCP morphology have been individually investigated, their synergistic effects have not been explored in any systematic manner. Interestingly, orientation response of BCP to changes in SE can be similar to what can be accomplished with variations in R. Here we present a novel approach for orienting lamellar BCP films of poly(styrene)-block-poly(methyl methacrylate) (PS-PMMA) on spin-coated xerogel (a dried gel of silica nanoparticle network) substrate with simultaneously tunable surface energy, {gamma}{sub s} {approx} 29-53 mJ/m{sup 2}, by UVO exposure and roughness, R{sub rms} {approx} 0.5-30 nm, by sol-gel processing steps of regulating the catalyst concentration and sol aging time. As in previous BCP orientation studies on 20 nm diameter monodisperse silica nanoparticle coated surface, we find a similar but broadened oscillatory BCP orientation behavior with film thickness due to the random rather than periodic rough surfaces. We also find that higher random roughness amplitude is not the necessary criteria for obtaining a vertical orientation of BCP lamellae. Rather, a high surface fractal dimension (D{sub f} > 2.4) of the rough substrate in conjunction with an optimal substrate surface energy {gamma}{sub s} 29 mJ/m{sup 2} results in 100% vertically oriented lamellar microdomains. The AFM measured film surface microstructure correlates well with the internal 3D BCP film structure probed by grazing incidence small-angle X-ray scattering (GISAXS) and rotational small-angle neutron scattering (SANS). In contrast to tunable self-assembled monolayer (SAM)-coated substrates, the xerogel films are very durable and retain their chemical properties over period of several months. These results also highlight importantly that BCP orientation control for nanotechnology is possible not only on specially prepared patterned substrates but also on industrially viable sol-gel substrates.
- Research Organization:
- Brookhaven National Lab. (BNL), Upton, NY (United States)
- Sponsoring Organization:
- USDOE SC OFFICE OF SCIENCE (SC)
- DOE Contract Number:
- DE-AC02-98CH10886
- OSTI ID:
- 1047000
- Report Number(s):
- BNL-94408-2012-JA; R&D Project: NC-001; TRN: US201215%%695
- Journal Information:
- Macromolecules, Vol. 45, Issue 10; ISSN 0024-9297
- Country of Publication:
- United States
- Language:
- English
Similar Records
Alignment frustration in block copolymer films with block copolymer grafted TiO2 nanoparticles under soft-shear cold zone annealing
Thin Film Self-Assembly of a Silicon-Containing Rod–Coil Liquid Crystalline Block Copolymer
Related Subjects
77 NANOSCIENCE AND NANOTECHNOLOGY
AGING
AMPLITUDES
CATALYSTS
CHEMICAL PROPERTIES
COPOLYMERS
FRACTALS
LAMELLAE
MICROSTRUCTURE
MORPHOLOGY
NEUTRONS
ORIENTATION
PROCESSING
ROUGHNESS
SCATTERING
SILICA
SOLAR CELLS
SOLS
STORAGE
SUBSTRATES
SURFACE ENERGY
THICKNESS
THIN FILMS
block copolymers
xerogel
roughness
GISAXS
RSANS