Synchrotron X-ray Study of Filled Skutterudites CeFe4Sb12 and Ce0.8Fe3CoSb12
In situ synchrotron X-ray diffraction measurements are carried out on filled skutterudites CeFe{sub 4}Sb{sub 12} and Ce{sub 0.8}Fe{sub 3}CoSb{sub 12} up to 32 and 20 GPa, respectively, at room temperature. No phase transformation was observed for both samples in the pressure range. Fitting the pressure-volume data (up to 10 GPa) to the third-order Birch-Murnaghan equation of state, the bulk modulus B{sub 0} is determined to be 74(4) GPa, with the pressure derivative B'{sub 0} = 7(2) for CeFe{sub 4}Sb{sub 12}, and B{sub 0} = 71(2) GPa and B'{sub 0} = 8(2) for Ce{sub 0.8}Fe{sub 3}CoSb{sub 12}. The bulk moduli of filled skutterudites CeFe{sub 4}Sb{sub 12} and Ce{sub 0.8}Fe{sub 3}CoSb{sub 12} in our study are smaller than those from previous studies on unfilled skutterudite CoSb{sub 3}. The P-V curves of the unfilled skutterudite CoSb{sub 3} and filled skutterudites CeyFe{sub 4-x}Co{sub x}Sb{sub 12} showed good agreement, indicating that the Ce filling fraction and the replacement of Fe with Co have little effect on their compression behaviors.
- Research Organization:
- Brookhaven National Lab. (BNL), Upton, NY (United States)
- Sponsoring Organization:
- USDOE SC OFFICE OF SCIENCE (SC)
- DOE Contract Number:
- DE-AC02-98CH10886
- OSTI ID:
- 1042065
- Report Number(s):
- BNL-97743-2012-JA; TRN: US201212%%476
- Journal Information:
- Physica B: Condensed Matter, Vol. 406, Issue 1; ISSN 0921-4526
- Country of Publication:
- United States
- Language:
- English
Similar Records
Thermoelectric properties of Ni-doped CeFe4Sb12 skutterudites
Structures and thermoelectric properties of double-filled (Ca{sub x}Ce{sub 1−x})Fe{sub 4}Sb{sub 12} skutterudites