Pulsed Laser CVD Investigations of Single-Wall Carbon Nanotube Growth Dynamics
- ORNL
- Duke University
The nucleation and rapid growth of single-wall carbon nanotubes (SWNTs) were explored by pulsed-laser assisted chemical vapor deposition (PLA-CVD). A special high-power, Nd:YAG laser system with tunable pulse width (> 0.5 ms) was implemented to rapidly heat (>30,000 C/s) metal catalyst-covered substrates to different growth temperatures for very brief (sub-second) and controlled time periods as measured by in situ optical pyrometry. Utilizing growth directly on transmission electron microscopy grids, exclusively SWNTs were found to grow under rapid heating conditions, with a minimum nucleation time of >0.10 s. By measuring the length of nanotubes grown by single laser pulses, extremely fast growth rates (up to 100 microns/s) were found to result from the rapid heating and cooling induced by the laser treatment. Subsequent laser pulses were found not to incrementally continue the growth of these nanotubes, but instead activate previously inactive catalyst nanoparticles to grow new nanotubes. Localized growth of nanotubes with variable density was demonstrated through this process, and was applied for the reliable direct-write synthesis of SWNTs onto pre-patterned, catalyst-covered metal electrodes for the synthesis of SWNT field-effect transistors.
- Research Organization:
- Oak Ridge National Lab. (ORNL), Oak Ridge, TN (United States). Center for Nanophase Materials Sciences (CNMS)
- Sponsoring Organization:
- USDOE Office of Science (SC)
- DOE Contract Number:
- DE-AC05-00OR22725
- OSTI ID:
- 1018569
- Resource Relation:
- Conference: 9th International Conference on Laser Ablation, Santiago de Teide, Tenerife, Canary Islands, Spain, 20070924, 20070928
- Country of Publication:
- United States
- Language:
- English
Similar Records
In situ time-resolved measurements of carbon nanotube and nanohorn growth
In Situ Laser Synthesis of Si Nanowires in the Dynamic TEM