Fracture of iron aluminide alloys
Five heats of iron aluminide alloys have been prepared, and their impact fracture properties compared to FA-129 iron aluminide. The first was a simple ternary alloy of iron, aluminum, and chromium to match the FA-129 composition. The second was similar but with additions of zirconium and carbon. The third alloy had zirconium, carbon, niobium and molybdenum. Two heats were produced produced with reduced aluminum contents so that a disordered body-centered cubic structure would be present. The impact properties, microstructures, and fractography of these alloys were compared to FA-129. The ductile-to-brittle transition temperatures of all of the Fe{sub 3}Al alloys were similar, but the simple ternary alloy had a much higher upper-shelf energy. The reduced aluminum alloys had lower transition temperatures. The microstructures were, in general, coarse and anisotropic. The fracture processes were dominated by second-phase particles.
- Research Organization:
- Oak Ridge National Lab., TN (United States)
- Sponsoring Organization:
- USDOE, Washington, DC (United States)
- DOE Contract Number:
- AC05-84OR21400
- OSTI ID:
- 10165442
- Report Number(s):
- CONF-9205123-11; ON: DE92017821
- Resource Relation:
- Conference: 6. annual fossil energy materials conference,Oak Ridge, TN (United States),12-14 May 1992; Other Information: PBD: [1992]
- Country of Publication:
- United States
- Language:
- English
Similar Records
Mechanical properties of iron-aluminum alloys
Tensile and impact properties of iron-aluminum alloys