Lightweight CO{sub 2}-resistant cements for geothermal well completions
Alkali metal catalyzed reactions between CO{sub 2}-containing brines and portland cement-based well cements can result in rapid strength reductions, increased permeability and casing corrosion, reduced well life, increased costs, and environmental concerns. Materials formed by acid-base reactions between calcium aluminate compounds and phosphate-containing solutions yield high strength, low permeability and CO{sub 2}-resistant cements when cured in hydrothermal environments. The cementing formulations are pumpable for several hours at temperatures up to 150C, thereby making their use for well completions technically feasible. When this cementing matrix was exposed in an autoclave containing Na{sub 2}CO{sub 3}-saturated brine for 120 days, < 0.4 wt% CaCO{sub 3} was produced. A conventional portland cement-based well completion material will form {approx} 10 wt% CaCO{sub 3} after only 7 days exposure. Addition of hollow aluminosilicate microspheres to the uncured matrix constituents yields slurries with densities as low as {approx} 1.2 g/cc which cure to produce materials with properties meeting the criteria for well cementing. Laboratory characterization is nearing completion, engineering scale-up is underway, and plans for field testing in a variety of geothermal fluids are being made.
- Research Organization:
- Brookhaven National Lab., Upton, NY (United States)
- Sponsoring Organization:
- USDOE, Washington, DC (United States)
- DOE Contract Number:
- AC02-76CH00016
- OSTI ID:
- 10151024
- Report Number(s):
- BNL-60326; CONF-9404102-2; ON: DE94011731
- Resource Relation:
- Conference: 12. geothermal program review: geothermal`s role in global climate change - impacts on the Climate Change Action Plan,San Francisco, CA (United States),25-28 Apr 1994; Other Information: PBD: [1994]
- Country of Publication:
- United States
- Language:
- English
Similar Records
Cementing of geothermal wells. Progress report No. 8, January--March 1978
The effect of Ca(OH)/sub 2/-treated ceramic microspheres on the mechanical properties of high-temperature lightweight cement composites