A review of irradiation effects on LWR core internal materials - neutron embrittlement.
- Environmental Science Division
Austenitic stainless steels (SSs) are used extensively as structural alloys in the internal components of light water reactor (LWR) pressure vessels because of their relatively high strength, ductility, and fracture toughness. However, exposure to neutron irradiation for extended periods not only changes the microstructure and microchemistry of these steels, but also degrades their fracture properties. The existing data on irradiated austenitic SSs are reviewed to determine the effects of key parameters such as material type and condition and irradiation temperature, dose, and dose rate on neutron embrittlement. Differences in the radiation-induced degradation of fracture properties between LWR and fast-reactor irradiations are also discussed. The results are used to (a) define a threshold fluence above which irradiation effects on fracture toughness of the material are significant, (b) evaluate the potential of neutron embrittlement under LWR operating conditions, and (c) assess the potential effects of voids on fracture toughness.
- Research Organization:
- Argonne National Lab. (ANL), Argonne, IL (United States)
- Sponsoring Organization:
- USNRC
- DOE Contract Number:
- DE-AC02-06CH11357
- OSTI ID:
- 1012533
- Report Number(s):
- ANL/EVS/JA-67660; TRN: US201110%%147
- Journal Information:
- J. Nucl. Mater., Vol. 412, Issue 1 ; May 2011
- Country of Publication:
- United States
- Language:
- ENGLISH
Similar Records
Crack growth rates and fracture toughness of irradiated austenitic stainless steels in BWR environments.
Fracture toughness evaluation of select advanced replacement alloys for LWR core internals